| Trade Name and Grade：PA6-GF25 HB251 Glass fiber reinforced |
| Properties | Test Standard | Test condition | Unit | Typical Value |
| Mechanical properties |
| Tensile strength | ISO527 | 5mm/min | MPa | 140 |
| Tensile Stain,Break | ISO527 | 5mm/min | % | 3 |
| Flexural strength | ISO178 | 2mm/min | MPa | 205 |
| Flexural modulus | ISO178 | 2mm/min | MPa | 6800 |
| Charpy notched impact strength | ISO179-1eA | 23℃ | KJ/m2 | 10 |
| Charpy impact strength | ISO179-1eU | 23℃ | KJ/m2 | 60 |
| Hardness | IOS2039 | 23℃ | N/mm2 | 180 |
| Thermal properties |
| Heat distortion temperature | ISO 75 | 1.8MPa | ℃ | 205 |
| Heat distortion temperature | ISO 75 | 0.45MPa | ℃ | 215 |
| Physical properties |
| Density | ISO1183 | 23℃ | g/cm3 | 1.32 |
| Other properties |
| Molding Shrinkage | ISO2577 | / | % | 0.3-0.5 |
| Filler content | ISO1172 | / | % | 25 |
| Address：No.369, Guangming Road, Zhuangshi Street, Zhenghai District, Ningbo. |
| Tel：(0574)87244771 Fax：(0574)87241375 |
| These technical data in the product brochures are typical data under specific test conditions( at 23±2℃ and 50±5% relative humidity) and not intended foruse as limiting specifications. |