| Trade Name and Grade：PC/ABS HX8500L Flame resistance |
| Properties | Test Standard | Test condition | Unit | Typical Value |
| Mechanical properties |
| Tensile strength | ISO527 | 50mm/min | MPa | 60 |
| Tensile Stain,Break | ISO527 | 50mm/min | % | 60 |
| Flexural strength | ISO178 | 2mm/min | MPa | 92 |
| Flexural modulus | ISO178 | 2mm/min | MPa | 2435 |
| Charpy notched impact strength | ISO179-1eA | 23℃ | KJ/m2 | 55 |
| Charpy impact strength | ISO179-1eU | 23℃ | KJ/m2 | NB |
| Thermal properties |
| Melt Index | ISO1133 | 260℃ 5KG | g/10min | 20 |
| Vicat softening temperature | ISO306 | 50℃/h,50N | ℃ | 105 |
| Heat distortion temperature | ISO 75 | 1.8MPa | ℃ | 94 |
| Heat distortion temperature | ISO 75 | 0.45MPa | ℃ | 103 |
| Physical properties |
| Density | ISO1183 | 23℃ | g/cm3 | 1.18 |
| Other properties |
| Flammability | UL94 | / | / | V0 |
| Molding Shrinkage | ISO2577 | / | % | 0.5-0.7 |
| Address：No.369, Guangming Road, Zhuangshi Street, Zhenghai District, Ningbo. |
| Tel：(0574)87244771 Fax：(0574)87241375 |
| These technical data in the product brochures are typical data under specific test conditions( at 23±2℃ and 50±5% relative humidity) and not intended foruse as limiting specifications. |
Follow Us